Description
LY3832 is a high-quality, two-component closed-cell polyurethane foam system specifically designed for pipe shell thermal insulation. This exceptional product is expertly premixed with HCFC-141b as a foaming agent, ensuring optimal performance and efficiency. Introducing our remarkable 4.4 Creep Resistance Rigid PU Polyurethane Polymeric Mdi and Polyol for Pipe Foam Insulation. This cutting-edge solution is meticulously formulated to meet the highest industry standards, providing superior thermal insulation for pipes. Our product boasts a unique combination of Polyether Polyol, Blend Polyol, and Polyol, resulting in unparalleled insulation properties. With its closed-cell structure, this foam system offers exceptional thermal conductivity, effectively reducing heat loss and ensuring energy efficiency. In addition to its exceptional insulation capabilities, our product also exhibits remarkable creep resistance. This means that it maintains its shape and performance over time, even under high pressure or stress conditions. This durability ensures long-lasting insulation for pipes, reducing maintenance costs and enhancing overall system efficiency. When it comes to pipe foam insulation, our 4.4 Creep Resistance Rigid PU Polyurethane Polymeric Mdi and Polyol stands out as the top choice. Its advanced formulation, combined with its closed-cell structure and exceptional creep resistance, guarantees outstanding thermal insulation performance. Choose our product for your pipe insulation needs and experience the highest level of quality, reliability, and efficiency. Trust in our expertise and let us provide you with the ultimate solution for your thermal insulation requirements.
Physical Properties
| Items |
Units |
LY3832 |
ISOCYANATE |
| Appearance |
|
Light yellow transparent liquid |
Brown liquid |
| Viscosity,25ºC |
mPa.s |
400-600 |
150-250 |
| Specific gravity,20ºC |
g/ml |
1.15±0.05 |
1.24±0.01 |
Reaction Performance(by hands)
| Items |
Units |
Specifications |
| LY3832 |
g |
100 |
| ISOCYANATE |
g |
140-160 |
| Cream time |
sec |
10-20 |
| Gel time |
sec |
/ |
| Track free time |
sec |
/ |
| Free rise density |
Kg/m3 |
30-40 |
Foam Performances
| Items |
Units |
Specifications |
Test Standard |
| Density |
Kg/m3 |
≥50 |
ASTM D1622 |
| Compressive strength |
kPa |
≥250 |
ASTM D1621 |
| Tensile strength |
kPa |
≥300 |
ISO 1926:2009 |
| Thermal conductivity,20ºC |
W/(m.k) |
≤0.024 |
ASTM C518 |
| Closed cell content |
% |
≥90 |
ASTM D2856 |
Dimensional Stability,-20ºC*24h
70ºC*90%RH*24h |
% |
≤2 |
ASTM D2126 |
The above testing data have been generated in lab or field conditions which are typical for this application. They are believed to be correct but data variations due to varying processing or ambient conditions can not be excluded. The customer remains responsible for making his own interpretation of data and suitability of the chemicals to his particular operation.
Handling and Storage
LY3832 should be protected from moisture by keeping containers sealed when not in use. Drums have to be stored indoors to protect the material from water ingress, frost and direct heat from the sun. Under temperature conditions and in properly sealed containers ,the storage life of the polyol is 6 months.
The optimum storage temperature should be 10-30ºC.