PE Low Friction Type Polyurethane Lamination Glue for Multilayer Pet/PE Film Limination

• Customization: Available
• Bonding Function: Structural Adhesive
• Morphology: Liquid
• Application: Packing
• Material: Polyurethane
• Classification: Room Curing
• Main Agent Composition: Natural Polymer
• Characteristic: Weatherability
• Promoter Composition: Curing Agent
• Composition: Organic Material
• Color: Clear
• Appearance: Yellowish Viscous Liquid
• Usage: Packing, Package, Bag, Structure
• Types of Substrates: CPP, BOPP, Mdope, LDPE, MDPE, Pet
• Temperature Resistance: 100-120ºC
• Packaging: 10/25/250 Kg/Barrel
• Transport Package: Drums, IBC Drums, Tank
• Specification: pure
• Trademark: G-TECH@
• Origin: China
• HS Code: 39095000
• Production Capacity: 20000mt/Year
• Package Size: 23.50cm * 23.50cm * 37.50cm
• Package Gross Weight: 21.500kg

Product Description

PE low friction type Polyurethane Lamination Glue for Multilayer PET/PE Film Limination

Product description
LY-6810A and LY-6810B are solvent-free two-component polyurethane adhesives, 100% solid content polyurethane adhesives for composite films, suitable for bonding various plastic films.
When the curing temperature of the composite PE film is higher than 40ºC, it will have a great impact on the solvent-free composite film with the inner layer of PE film (especially when PE film thickness is <45μm), and the friction coefficient is likely to increase significantly.
Because the higher the curing temperature, the more intense the molecular motion of the slip agent in the PE film, and the molecular is easy to move to the adhesive layer and react with it to be consumed, which eventually leads to an increase in the coefficient of friction of the composite film. This product can perfectly solve this problem.

Instructions

Applicable models:	Any model of solvent-free compounding equipment
Weight ratio:	/
Coating amount:	/
Operating temperature:	/
Available in:	0-40 min

Technical parameter

Model	LY6810A	LY6810B
Component	Isocyanate	hydroxyl
Appearance	Light yellow to yellow transparent liquid	Light yellow to yellow transparent liquid
Solid content	100%	100%
Viscosity 45ºC(mPa• s)	<1500	<1000
Density 35-40ºC(g/cm3)	1.19±0.01	1.14±0.01

Performance index
LY6810A/LY6810B (mixed by weight at a ceratin ratio) can be used for typical flexible packaging structure; peel strength after fully cured (N/15mm):

Structure	48h at 40ºC-45ºC
PET/CPP	/
PET/PE	/
NY/PE	/
OPP/CPP	/

Friction coefficient:

Outside of PE	Static friction coefficient	kinetic friction coefficient
Change after coating	/	/
Outside of CPP	/	/
Change after coating	/	/

Packaging and storage
LY-6810A: 20Kg/barrel; LY-6810A: 200Kg/barrel
LY-6810B: 20Kg/barrel; LY-6810B: 200Kg/barrel
In a dry and clean environment of 5ºC-30ºC, unopened products can be stored for at least 6 months. Unused products after opening must be sealed and stored and used up as soon as possible.