Plastic Granule Polyurethane/PU TPU Resin Excellent Hydrolysis Resistance Polycaprolactone Based TPU for Sealing Rings

• Molecular Principal Chain: Urethane Based Polymer
• Color: White
• Form: Oval Particles
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: J series
• Hardness,Shore a: 55-95
• Density,g/cm3: 1.19-1.22
• Tensile Strength,MPa: 38-60
• Tear Strength,MPa: 110-220
• Elongation at Break,%: 300-550
• Tg,°c: -42~-30
• 100% Modulus,MPa: 5-34
• 300% Modulus,MPa: 10-45
• Transport Package: Paper-Plastic Bags
• Specification: pure
• Trademark: G-TECH@
• Origin: China
• HS Code: 39095000
• Production Capacity: 10000mt/Year
• Package Size: 77.00cm * 44.00cm * 15.00cm
• Package Gross Weight: 25.100kg

Product Description

Plastic granule Polyurethane/PU TPU resin excellent hydrolysis resistance Polycaprolactone Based TPU for sealing rings


Performance characteristics
excellent hydrolysis resistance, oil resistance, abrasion resistance, resilience and low temperature flexibility


Applications
sealing rings, casters


Reference index

Properties		Standard	Unit	J60	J65	J80	J85	J45	J46	J75
Density		ASTM D792	g/cm^3	1.19	1.19	1.19	1.20	1.21	1.21	1.22
Hardness		ASTM D2240	Shore A/D	82/-	86/-	92/-	95/-	-/55	-/65	-/75
Tensile Strength		ASTM D412	MPa	/	/	/	/	/	/	/
100% Modulus		ASTM D412	MPa	/	/	/	/	/	/	/
300% Modulus		ASTM D412	MPa	/	/	/	/	/	/	/
Elongation at Break		ASTM D412	%	/	/	/	/	/	/	/
Tear Strength		ASTM D624	kN/m	/	/	/	/	/	/	/
DIN Abrasion Loss		DIN 53516	mm^3	/	/	/	/	/	/	/
Tg		DSC	ºC	/	/	/	/	/	/	/
Compression Set	22 hours@70ºC	ASTM D395	%	/	/	/	/	/	/	/
	24 hours@100ºC	ASTM D395	%	/	/	/	/	/	/	/

Note:The above values are shown as typical values and should not be used as specifications.