Rigid Polyurethane Foam PIR System Polyether Polyol for Composite Panel Insulation

• Molecular Principal Chain: Naphthenic Polymer
• Color: Brown
• Appearance: Light Yellow Transparent Viscous Liquid
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: LYR1716
• Hydroxyl Value Mgkoh/G: 400-500
• Dynamic Viscosity (25ºC) MPa.S: 400-600
• Density (20ºC) G/Ml: 1.1±0.02
• Storage Temperature ºC: 10-25
• Transport Package: Steel Drum/IBC Drum/Tank
• Specification: pure
• Trademark: G-TECH@
• Origin: China
• Production Capacity: 50000mt/Year
• Package Size: 60.00cm * 60.00cm * 102.00cm
• Package Gross Weight: 218.000kg

Product Description

DESCRIPTION
LYR1716 is a blend of polyols,surfactants,catalysts,fire retardant and CFC free blowing agent.The polyol offers increased resistance to burning and spread of flames.The polyol blend is specifically developed as one part of a two components system for rigid polyurethane insulated pannel processed by filling with dispensing machine or by mutual pouring in place.
It is widely used in manufacture of composite board,sandwich panel,inorganic panel applied for door,outwall,roofing,air condition duct and so on. 
The foam of this PIR system has a good flowability, low thermal conductivity, good dimensional stability and excellent fire resistance properties.

PHYSICAL and CHEMICAL PROPERTIES    

	POLYOL COMPONENT	MDI-ISOCYANATE COMPONENT
Apperance	Clear amber liquid	Dark brown viscous liquid
Viscosity@20ºC	500±100cps	200±40cps
Hydroxyl value	400±50mgKOH/g	/
Specific gravity@20ºC	1.15±0.05gm/cc	1.23gm/cc
MIX RATIO (lab trials suggest following formulation)	100pbw	150-180pbw(adjustable)

RECOMMENDED PROCESS CONDITIONS
System temperature:20±2ºC
Compoment temperature:22±2ºC
Mould temperature:30-35ºC
TYPICAL FORM PERFORMANCE                  
 

Testing items	Test method		Index
	Chinese standard	Referance Standard
Moulded Density (kg/m3) ≥	GB/T 6343-2009	ISO 845:2006	45
Closed-cell rate (%)  ≥	GB/T10799-2008	ISO 4590:2002	90
Initial Thermal conductivity (W/m.k)       ≤	GB/T 10295-1988	ISO 8301:1991(E)	0.023
Compressive strength     ≥	GB/T 8813-2008	ISO 844:1978	200
Dimensional stability (%)	GB/T 8811-2008	ISO 2796:1980	2

BURNING CHARACTERISTICS           

Self extinguishing to (DIN-4102)

Classification-B1

HANDLING and STORAGE               
LYR1716 Polyol and PU systems should be stored at room temperature below 25ºC in sealed drums.Agitate contents before use particularly after long standing.Precautions should be observed to avoid prolonged or repeated skin contact with the products or its introduction in or near to the eyes.If skin contact occurs all contaminated clothing should be removed and the effected skin area wiped with a cloth or paper towels saturated with ethanol or equivalent solvent followed by washing with soap and water.Goggle or eye shields should be worn when there is a danger of splashing or eye contact.With the exercise of such care LYR1716 System should not present any undue hazard to health under normal working conditions(Protective clothing and eye protection is recommended when handling Polyol).