Flexible PU/Polyurethane Conventional Polyol for Flexible Foam

• Customization: Available
• Molecular Principal Chain: Naphthenic Polymer
• Color: Brown
• Model NO.: DEP-560L
• Hydroxyl Value Mgkoh/G: 54.5-57.5
• Water Max,%: ≤0.05
• Acid Value Mgkoh/G: ≤0.05
• pH Value: 5-7
• Viscosity MPa·s,25ºC: 400-700
• K+,Na+ Max,Mg/G: Not Detected
• Chroma Apha: ≤50
• Transport Package: Steel Drum/IBC Drum/Tank
• Specification: pure
• Trademark: G-TECH@
• Origin: China
• Production Capacity: 50000mt/Year
• Package Size: 60.00cm * 60.00cm * 102.00cm
• Package Gross Weight: 228.000kg

Product Description

Flexible PU/Polyurethane Conventional Polyol for Flexible Foam
 

Conventional Polyether Polyol for Flexible Foam
Model No.	Hydroxyl value	Water	Acid value	PH value	Viscosity	K+,Na+	Chroma	Remark
	mgKOH/g	Max,%	mgKOH/g		mPa·S,25ºC	Max,mg/g	APHA
DEP-560L	54.5-57.5	≤0.05	≤0.05	5-7	400-700	Not detected	≤50	DEP-560L is a polyether polyol with a molecular weight of 300 and made of metal catalyst. It is mainly used to produce soft block sponges.
DEP-348	46.5-49.5	≤0.05	≤0.05	5-7	550-750	Not detected	≤50	DEP-348 is a polyether polyol with a functionality of 3 and no BHT, a molecular weight of 3500, and made of bimetallic catalyst. It is mainly used to produce soft block sponges.

HANDLING PRECAUTIONS
Flash point is above 200 degree centigrade (open cup method), flammable but non-explosive. In case of
fire, put out with foams, dry powder, steam or water.
When handling polyols, precautions should be taken to avoid exposure to the eye or prolong contact
with the skin. If eye contact occurs, flush with plenty of water. If skin contact occurs, wash exposed areas
thoroughly with soap and water.

STORAGE
It is slightly hygroscopic and may absorb water. Containers should be kept sealed and protected
from contamination of moisture and foreign materials.
The shelf life is 6 months. After that, the pre-test should be made before use.

Package:
Steel drum/IBC drum/Isotank           

Shelf Life: 
The shelf life is 6 months. After that, the pre-test should be made before use.