Rigid PU Polyurethane Raw Building Materials Polyurethane Foam Chemical for Continous Sandwich Panel

• Customization: Available
• Molecular Principal Chain: Naphthenic Polymer
• Color: Brown
• Model NO.: DFR713F3
• Viscosity@20℃: 200-250cps
• Specific Gravity@20℃: 1.21±0.01GM/Cc
• Oh Content: 370 Mgkoh/G
• Nco: 30-32%
• Mixing Ratio: 100:125-140
• Free Rise Density,Kg/M3: 32-33
• Packing: Blend Polyol in 220kg Drums
• Transport Package: Steel Drum/IBC Drum/Tank
• Specification: pure
• Trademark: G-TECH@
• Origin: China
• HS Code: 390931
• Production Capacity: 30000mt/Year
• Package Size: 60.00cm * 60.00cm * 102.00cm
• Package Gross Weight: 218.000kg
• Lead Time: 3 days (1 - 5000 kg) ; To be negotiated ( > 5000 kg)

Product Description

POLYOL BLEND DFR713F3

DFR713F3 is a formulated polyol consisting of,surfactants,catalysts,fire retardant and N-pen tane blowing agent. The polyol blend is specifically developed as one part of a two components system for rigid polyurethane insulated pannel with continuous process.
It is widely used in manufacture of composite board,sandwich panel,inorganic panel applied for door,wall,roofing,air condition duct and so on.
Panels manufactured with DFR713F3 system will display higher degree of compression and tensile strength in addition to its thermal and Eco-Efficiency performance.The higher percentage of closed cell is considered excellent barrier for air,water and noise.

PHYSICAL and CHEMICAL PROPERTIES    

	POLYOL	ISOCYANATE	Test Method
Apperance	Clear amber liquid	Dark brown viscous liquid
Viscosity@20ºC	200-250cps	170-230cps	ASTM D445
Specific gravity@20ºC	1.21±0.01gm/cc	1.23±0.01gm/cc	ASTM D891
OH content	370 mgKOH/g		ASTM 4274
NCO		30-32%	ASTM D5155
Mixing ratio	100	125-140

RECOMMENDED PROCESS CONDITIONS
System temperature:/
Compoment temperature:/
Mould temperature:/

TYPICAL REACTION PROPERTIES         

	Units	Handmix	PACKING
Cream Time,sec	S	/
Gel Time,sec	S	/	Blend Polyol in 220kg drums
Track Free Time,sec	S	/
Free Rise Density,kg/m3	Kg/m^3	32-33	ISO/MDI in 250kg drums

FORM PERFORMANCE                   

Testing Items	Test method		Index
	China standard	Referance Standard
Closed-cell Rate (%)  ≥	GB/T10799-2008	ISO 4590:2002	qualified
Initial Thermal Conductivity (W/m.k)    ≤	GB/T 10295-1988	ISO 8301:1991(E)	qualified
Compressive Strength     ≥	GB/T 8813-2008	ISO 844:1978	qualified
Dimensional Stability (%)	GB/T 8811-2008	ISO 2796:1980	qualified
48h  70°C     ≤
48h  -30°C    ≤			qualified

HANDLING and STORAGE               
DFR713F3 Polyol and PU systems should be stored at room temperature below 25ºC in sealed drums.Agitate contents before use particularly after long standing.Precautions should be observed to avoid prolonged or repeated skin contact with the products or its introduction in or near to the eyes.If skin contact occurs all contaminated clothing should be removed and the effected skin area wiped with a cloth or paper towels saturated with ethanol or equivalent solvent followed by washing with soap and water.Goggle or eye shields should be worn when there is a danger of splashing or eye contact.With the exercise of such care DFR713F3 System should not present any undue hazard to health under normal working conditions(Protective clothing and eye protection is recommended when handling Polyol).